Welding Cast Iron can make a preacher cuss. Aluminum Bronze covers a multitude of sins AC are you crazy Cast iron is hard to weld. Golf is hard too. But welding cast iron is kind of like playing golf. Every now and then you have a good day and you are lulled into thinking its not so bad. That is because welding cast iron is like flipping a coin. One job goes pretty goodthe next job makes you cuss. Why is that 2 main reasons. There are many different grades of cast iron, some more weldable than others. And it is difficult to tell them apart. By looking at the sparks it makes when grinding, and also by looking at a fractured surface some old timers can tell the difference in cast iron. Website X5 Free Download Keygen Corel here. But that guy is rare. In fact, when is that last time you talked to an old timer welder about welding. Oh snap I just realized something. I am an old timer myself now. Son of a gun What an epiphany With well over 3. I dont feel that old some daysat least I still take the stairs 2 at a time. The environment the cast iron has been in makes more difference than anything else. Exhaust manifolds are by far the hardest cast iron welding job to tackle because they are just flat impregnated with carbon from years of heating and cooling and being exposed to burning fuel exhaust. Welding A Cracked Exhaust Manifold' title='Welding A Cracked Exhaust Manifold' />VVC heads. The VVC head is a superior casting which as well as containing the VVC mechanisms also has larger valves 31. I have had an exhaust leak on my trusty Skoda for a while, I can hear it coming from miles away My problem was that to find the leak with the engine running was. Welding a broken cast iron leg off of grandmas old pot belly stove is easy. It has not been exposed to hot gases for 2. Except for Uncle Percys long boring stories. It broke because Uncle Percy, tripped over his spit cup and knocked it over. Once you weld the cast iron leg back on, if Uncle Percy trips again, it will break again. If not, it will be good to go for years to come. On the other hand, The exhaust manifold from Uncles Percys boat motor. You know, The outboard that he bought used 3. That one is not going to be so easy. I did pull this out of my rectal database and have no expertise in fixing boat motors. Enough BSSo what is the best way to weld cast iron The way you can make work. I have my own little secret for welding cast iron and I will tell you in a minute. Lets look at some real simple metallurgy. Mild steel has less than 0. Thats 0. 2 or 2 tenths of 1 percent. Thats not much. Medium carbon steel has more than 0. Cast iron has anywhere from 3 to 8 full percent of carbon. Thats way more than 1. And will get as hard as Japanese arithmetic when you weld it if you are not careful. Brittle too This is why often times when you weld cast iron, you hear it crack somewhere away from the weld. The weld metal shrinks and stresses the brittle cast iron around it enough to crack it. So how do we combat this Here is what I do. Clean the metal. This means groove out the crack, and grind to shiny bright metal all around past where any welding goes on. Preheat if possible. If the part is small enough, an old gas grill bought on craigslist strictly just for preheating cast iron would work great. London broil wont taste funny. This gas grill was advertised in craigslist for FREE. It would make a great preheat and post heat oven. There are 2 thoughts here. If the part is too big to preheat, still clean and groove out crack, but keep heat input to a minimum. But Most parts I see can be preheated. And when you can preheat, do it. Then whats the best way to weld it Here is my little secret Are you ready I tig weld on AC with AC balance control maxed out and use Aluminum Bronze filler metal. Its strong, it flows really well on AC, dilution is low, and shrinkage stress is low so it does not tend to crack other areas next to the weld. This method works great for tractor and farm equipment and machinery, But may not work as well when you have a lot of thermal cycles like on an engine. For that type of application My choice would be to stick weld using a nickel rod also known as Ni Rod. Ni is pronounced likeeye with an N. Sometimes the flux on the stick electrode can help dissolve some of the excess carbon. Another possibility that I have experimented with is to Mig weld cast iron. If you are going to try this, you need a ball peen hammer in one hand and the mig gun in the other. As soon as you finish a short bead and while the bead is still red hot, peen the weld bead with the ball end of the hammer. This helps combat the shrinkage of the weld metal. I have also experimented with some success, using a small mig welder and feeding extra nickel rod in like I was tig welding to keep the weld from hardening. HAH I bet you never thought of doing that. I have also tig welded cast iron with high nickel tig rods with some success, and I have even beat the flux off a Ni rod and tig welded cast iron. Bottom line is still the same, one cast iron welding job goes good, the next one makes you question the meaning of life. The filler metal designation is ERCu. Al A2 in case you want to google it or ask your local welding supply for it.